1.4541 Steel Material X6CrNiTi18-10 EN1092-1 TYPE 01 Plate Flange
| Minimum Order Quantity | 1 pcs |
|---|---|
| Price | 0.2 usd/pcs |
| Packaging Details | standard exported package |
| Delivery Time | 5-8 working days |
| Payment Terms | L/C, D/A, D/P, T/T, Western Union, MoneyGram |
| Supply Ability | 10000 pcs in stock |
Contact me for free samples and coupons.
Whatsapp:0086 18588475571
Wechat: 0086 18588475571
Skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xProduct Details
| Material | 1.4541 | Type | Plate Flange |
|---|---|---|---|
| Standard | EN1092 Type 01 | China Material | X6CrNiTi18-10 |
Product Description
1.4541 Steel Material X6CrNiTi18-10 EN1092-1 TYPE 01 Plate Flange
| Grade : | X6CrNiTi18-10 | ||||||||||||||||
| Number: | 1.4541 | ||||||||||||||||
| Classification: | Austenitic stainless steel | ||||||||||||||||
| Density: | 7.9 g/cm ³ | ||||||||||||||||
| Standard: |
|
1.4541 Steel Plate Flange Chemical composition % of steel X6CrNiTi18-10 (1.4541): EN 10088-2-2005
| Ti = 5 * C to 0.7 Particular ranges of sulphur content may provide improvement of particular properties. For machinability a controlled sulphur content of 0.015 % to 0.030% is recommended and permitted. For weldability, a controlled sulphur content of 0.008 % to 0.030 % is recommended and permitted. For polishability, a controlled sulphur content of 0.015 % max is recommended. Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. |
| C | Si | Mn | Ni | P | S | Cr | Ti |
| max 0.08 | max 1 | max 2 | 9 - 12 | max 0.045 | max 0.015 | 17 - 19 | max 0.7 |
| Rm - Tensile strength (MPa) (+A) | 500-720 |
| Rm - Tensile strength (MPa) (+AT+C) | 810-850 |
| Rm - Tensile strength (MPa) (+AT) | 460-730 |
| Rp0.2 0.2% proof strength (MPa) (+A) | 190-225 |
| Rp0.2 0.2% proof strength (MPa) (+AT) | 180-200 |
| KV - Impact energy (J) transverse, (+A) | +20° 60 |
-196° 60 |
| KV - Impact energy (J) longitud., (+A) | +20° 100 |
| A - Min. elongation at fracture (%) (+A) | 30-40 |
| A - Min. elongation at fracture (%) longitud., (+AT) | 35 |
| Nominal diameter (mm): | 2 - 50 |
| Z - Reduction in cross section on fracture (%) | 60-65 |
| Brinell hardness (HB): (+A) | 215 |
| Brinell hardness (HB): (+AT) | 210 |